pc940物性表-LEXAN 940 照明部件PC- 规格:25KG/包
pc940物性表Lexan* Resin 940
Americas: COMMERCIAL
Opaque colors, medium viscosity, superior flame retardance.
TYPICAL PROPERTIES¹ TYPICAL VALUE Unit Standard
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min 630 kgf/cm² ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 560 kgf/cm² ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 90 % ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 920 kgf/cm² ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 22800 kgf/cm² ASTM D 790
Hardness, Rockwell M 70 - ASTM D 785
Hardness, Rockwell R 118 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044
IMPACT
Izod Impact, unnotched, 23°C 326 cm-kgf/cm ASTM D 4812
Izod Impact, notched, 23°C 65 cm-kgf/cm ASTM D 256
Tensile Impact, Type S 535 cm-kgf/cm² ASTM D 1822
Falling Dart Impact (D 3029), 23°C 1728 cm-kgf ASTM D 3029
THERMAL
Vicat Softening Temp, Rate B/50 151 °C ASTM D 1525
HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648
CTE, -40°C to 95°C, flow 6.84E-05 1/°C ASTM E 831
Thermal Conductivity 0.19 W/m-°C ASTM C 177
Relative Temp Index, Elec 130 °C UL 746B
Relative Temp Index, Mech w/impact 120 °C UL 746B
Relative Temp Index, Mech w/o impact 130 °C UL 746B
LEXAN PC沙伯基础创新塑料 940现货报价
低收缩韧性好高流动高透明易脱模高刚性食品级抗紫外线电气性好玻纤增强阻燃
PC在汽车上的应用,预计2005年中国汽车总量达300多万辆，需求量达到3万t，因而聚碳酸酯在这一领域的应用是极有拓展潜力的。
PC的医疗级PC料可制作成注射器.
PC应用于医疗器械:由于聚碳酸酯制品可经受蒸汽、清洗剂、加热和大剂量辐射消毒，且不发生变黄和物理性能下降，因而被广泛应用于人工肾血液透析设备和其他需要在透明、直观条件下操作并需反复消毒的医疗设备中。
山东LEXAN PC沙伯基础创新塑料 940代理商价格