Lexan* Resin 241R物性表
Americas: COMMERCIAL
General purpose polycarbonate with 10.5 MFR and internal mold release.
TYPICAL PROPERTIES¹ TYPICAL VALUE Unit Standard
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min 630 kgf/cm² ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 700 kgf/cm² ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 130 % ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 980 kgf/cm² ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 23900 kgf/cm² ASTM D 790
Hardness, Rockwell M 70 - ASTM D 785
Hardness, Rockwell R 118 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044
IMPACT
济南pc基础创新塑料241r价格
Izod Impact, unnotched, 23°C 326 cm-kgf/cm ASTM D 4812
Izod Impact, notched, 23°C 81 cm-kgf/cm ASTM D 256
Tensile Impact, Type S 589 cm-kgf/cm² ASTM D 1822
Falling Dart Impact (D 3029), 23°C 1728 cm-kgf ASTM D 3029
Instrumented Impact Energy @ peak, 23°C 650 cm-kgf ASTM D 3763
THERMAL
Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525
HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648
CTE, -40°C to 95°C, flow 6.84E-05 1/°C ASTM E 831
Specific Heat 1.25 J/g-°C ASTM C 351
Thermal Conductivity 0.27 W/m-°C ASTM C 177
Relative Temp Index, Elec 130 °C UL 746B
台州pc基础创新塑料241r报价
PC聚碳酸酯材料介绍:
聚碳酸酯(PC)是一种无定形热塑性PC工程塑料。它具有极为优良的韧性、透明度和高的热变形温度等综合性能。在大多数应用中，一般都要求至少有上述这样性能中的两种。聚碳酸酯其他杰出的性能还有尺寸稳定性、优良的电性能和特有的耐燃性。主要应用领域为汽车、商业机器和仪表行业。聚碳酸酯年增长率约为6%。
PC聚碳酸酯PC的一般特性归纳如下:
1. 出色的物理特性
2. 出色的韧性
3. 非常好的耐热性
4. 抗化学作用能力一般
5. 透明
6. 中高价位
7. 较易加工